How to make acrylic jewelry stands by hot bending?

Acrylic products will be softer after hot bending, and the shape will be more varied. There is no seam after hot bending, the shape is smooth, the appearance is beautiful and generous, and it will not deform and break for a long time. It is widely loved by people, so many acrylic products now need to be hot-bent in the production.

In the hot bending process, according to the different needs of the shape, there are two kinds of local hot bending and overall hot bending.

The overall hot bending process is to heat all the acrylic sheets, this step is required to enter the oven. In this process, the acrylic product needs to be put into the oven. When the temperature in the oven rises to the melting point of the acrylic, the acrylic sheet will slowly soften, and then the acrylic product is placed on the mold, and finally the cooling will be completely applied to the mold. on. It should be noted at that time that the temperature of the oven is also controlled and cannot be raised too high at one time. After the hot melt, the acrylic gradually hardens when it encounters the cold air, and begins to form.

Local hot bending is one of the more common ones used in the hot bending process of acrylic products. The most common is to bend the acrylic of a straight plate out of a curve, like a circle, a curve, and so on. There are also some cumbersome local hot bends, such as bending an acrylic heat into a right angle, but the hot bend is a smooth arc. This process is to remove the sticker attached to the acrylic plate in this hot bend. The high-temperature mold rod is used to fuse the edge of the acrylic that needs to be bent, and then bend it into a right angle with an external force. The edge of the acrylic product thus produced is a smooth curved right angle.